JOTACRYL WHITE – 4 L

Type : This product is a glossy solvent based acrylic topcoat.

Features and benefits : Provides washable, high gloss finish.

Recommended use : Ideal as a topcoat in Texotile system.

Substrate : Cement plaster, concrete, block work, rendered surfaces, gypsum board etc.

Product data

Packaging size : 4 L

Colours : White

Solids by volume : 34 ± 2 volume% Theoretical

Specific gravity : 1.15 Only for white colour.

Flash point : Closed cup: 25°C (77°F)

VOC : 577 g/l ISO 11890 EU

VOC 577 g/l US EPA method 24.

VOC comments : This is the theoretical value. Tested value will vary depending on test methodology, accuracy of equipment used for testing and test conditions.

Application data
The product can be applied by
Roller : Recommended.
Spray : Use airless spray or conventional spray.
Brush : Recommended to paint corners and edges.

Guiding data for airless spray
Nozzle tip 0.018–0.021″
Spray angle degrees 65–80°
Pressure at nozzle 15 MPa (150 kp/cm², 2100 psi)

Cleaning of painting tools : Water

Film thickness per coat
Typical recommended range
Dry film thickness 30 – 40 μm
Wet film thickness 90 – 120 μm
Film thickness will vary and is calculated as average.
Theoretical spreading rate 11.5 – 8.5 m²/l
Spreading rate depends on film thickness applied, type of texture, surface porosity, imperfections, temperature, wastage during painting etc.
Maximum spread rate per coat is obtained at minimum dry film thickness and vice versa.

Thinner : Jotun Thinner No. 7
Dilution : Maximum 10 %

Conditions during application
The temperature of the substrate should be minimum 10 °C and at least 3 °C above the dew point of the air, measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The moisture content in the substrate should not exceed 4 % (by weight). The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Drying times
Drying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly.
1. Recommended data given is, for recoating with the same generic type of paint.
2. In case of multi-coat application, drying times will be influenced by the number and sequence and by the total thickness of previous coats applied.
3. The surface should be dry and free from any contamination prior to application of the subsequent coat.

The drying time is measured by stated values:
Relative Humidity (RH) 50 % Substrate temperature 10 °C 23 °C 40 °C

Surface (touch) dry              6 h 3 h 1 h
Hard dry                             10 h 5 h 3 h
Dry to over coat, minimum   6 h 3 h 1 h

Directions for use
Surface preparation
The substrate must be sound, clean, dry and free from dust, oil, grease, laitance etc. All traces of form release agents/curing agents must be removed. A light sanding with suitable abrasive material is recommended before application. Any resulting dust/loose particles must be removed.

Remarks : Other systems may be specified, depending on area of use. Contents of packaging with different batch numbers must be mixed together before use. Please refer to the Decorative Sales Department for technical advice.

Storage
The product must be stored in accordance with national regulations. Keep the containers in a dry, cool, well ventilated space and away from sources of heat and ignition. Containers must be kept tightly closed. Handle with care.

Disclaimer
The information in this document is given to the best of Jotun’s knowledge, based on laboratory testing and practical experience. Jotun’s products are considered as semi-finished goods and as such, products are often used under conditions beyond Jotun’s control. Jotun cannot guarantee anything but the quality of the product itself. Minor product variations may be implemented in order to comply with local requirements. Jotun reserves the right to change the given data without further notice.

Users should always consult Jotun for specific guidance on the general suitability of this product for their needs and specific application practices.